Vagatio Directa pro LFT
Vagatio Directa pro LFT
Stratura directa pro LFT obducitur impletione silanica, quae cum resinis PA, PBT, PET, PP, ABS, PPS et POM congruit.
Proprietates
●Lanugo humilis
● Excellens compatibilitas cum resina thermoplastica multiplici
● Bona proprietas processus
● Proprietates mechanicae excellentes producti compositi finalis
Applicatio
Late adhibetur in autocinetis, constructione, ludis athleticis, electricis et electronicis applicationibus.
Index Productorum
| Res | Densitas Linearis | Compatibilitas Resinae | Proprietates | Usus Finalis |
| BHLFT-01D | 400-2400 | PP | Bona integritas | Excellens processus et proprietas mechanica, color lucis extinctus |
| BHLFT-02D | 400-2400 | PA, TPU | Lanugo humilis | Excellens processus et proprietas mechanica, ad processum LFT-G destinata |
| BHLFT-03D | 400-3000 | PP | Bona dispersio | Specialiter ad processum LFT-D designatum et late in autocinetis, constructione, ludis athleticis, applicationibus electricis et electronicis adhibitum |
| Identificatio | |||||
| Genus Vitri | E | ||||
| Vagatio directa | R | ||||
| Diameter filamenti, μm | quadringenti | DC | 1200 | 2400 | tria milia |
| Densitas linearis, tex | 16 | 14 | 17 | 17 | 19 |
| Parametri Technici | |||
| Densitas Linearis (%) | Contentum Humoris (%) | Magnitudo Contenta (%) | Robur Fracturae (N/Tex) |
| ISO1889 | ISO3344 | ISO1887 | IS03341 |
| ±5 | ≤0.10 | 0.55±0.15 | ≥0.3 |
Processus LFT
Granula polymerica LFT-D et vitrea fibra omnia in extrusorem bicochlearem immittuntur, ubi polymerum liquefacitur et compositum formatur. Deinde compositum liquefactum directe in partes finales per iniectionem vel processum formationis compressivae fingitur.
Polymerum thermoplasticum LFT-G ad phasem liquefactam calefactum et in caput filamenti immittitur. Filum continuum per matricem dispersionis trahitur ut fibra vitrea et polymerum plene impregnentur et virgae consolidatae fiant. Post refrigerationem, virga in granula firmata dividitur.